A Novel Route to Synthesis Silica Hollow Spheres Having Zsm-5 Structure in Absence of Template

N. Venkatathri

Composite Materials Center, Korea Institute of Ceramic Engineering and Technology, 233-5, Gasan-Dong, Guemcheon-Gu, Seoul 153-801, (South Korea)

Article Publishing History
Article Received on :
Article Accepted on :
Article Metrics
ABSTRACT:

A novel route to synthesize silica hollow spheres with thick walls having ZSM-5 structure without using any template at 140oC was presented. X-ray diffraction (XRD), Scanning electron microscopy (SEM), TG/DTA, FT-IR and nitrogen adsorption were employed to characterize the morphology and microstructures of the as-prepared silica hollow spheres. Experimental results indicated that the hollow spheres had an average diameter of nearly 200 nm with a surface area of 342 m2/g.

KEYWORDS:

Silica hollow spheres; ZSM-5; without template; Synthesis

Download this article as: 

Copy the following to cite this article:

Venkatathri N. A Novel Route to Synthesis Silica Hollow Spheres Having Zsm-5 Structure in Absence of Template. Orient J Chem 2006;22(2).


Copy the following to cite this URL:

Venkatathri N. A Novel Route to Synthesis Silica Hollow Spheres Having Zsm-5 Structure in Absence of Template. Orient J Chem 2006;22(2). Available from: http://www.orientjchem.org/?p=19439



Creative Commons License
This work is licensed under a Creative Commons Attribution 4.0 International License.

About The Author